• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-1351-4225
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0132
  • Page Number : 19-28
  • Doi : 10.12739/NWSA.2018.13.1.2A0132
  • Abstract Reading : 576
  • Download : 131
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 1
  • Number of Articles Published : 7
  • Published Date : 1.01.2018

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

TOOLOX 44 MALZEMESİNDE TALAŞ KALDIRMA MİKTARININ YÜZEY PÜRÜZLÜLÜĞÜ VE TAKIM AŞINMASI ÜZERİNDEKİ ETKİLERİNİN İNCELENMESİ

Rüstem BİNALİ1 , Hasan Basri ULAŞ2 , Halil DEMIR 3

Bu çalışmada, gelişen imalat sektöründe kullanılmak üzere yeni üretilen Toolox 44 sıcak iş takım çeliği (44 HRC) kullanılarak işlenebilirlik deneyleri gerçekleştirilmiştir. İşlenebilirlik deneylerinde, kaldırılan talaş miktarına göre iş parçası yüzeyindeki yüzey pürüzlülüğü, deney sırasında oluşan kesme kuvveti ve kesici takımda oluşan takım aşınması incelenmiştir. Yapılan deneyler yüzey frezeleme yöntemiyle dört farklı kesme hızında (150-180-210-240m/dak), dört farklı ilerleme miktarında (0.4, 0.8, 1.2, 1.6mm/diş) ve iki farklı talaş derinliğinde (0.2-0.4mm) soğutma sıvısı kullanılmadan gerçekleştirilmiştir. Aşınma deneylerinde ise kaldırılan talaş hacmine (320-1600-3200-6400mm3) göre incelemeler gerçekleştirilmiştir. Sonuçlar neticesinde ilerleme miktarının ve kesme hızının artmasıyla yüzey pürüzlülük değerinin arttığı, kesme kuvveti değerlerinin ise ilerleme miktarına bağlı olarak arttığı kesme hızının artmasına bağlı olarak da azaldığı görülmüştür.

Keywords
TOOLOX 44, Yüzey Pürüzlülüğü, Takım Aşınması, Talaş Miktarı, Aşınma,

INVESTIGATION OF THE EFFECTS ON SURFACE ROUGHNESS AND TOOL WEAR IN THE TOOLOX 44 MATERIAL

Rüstem BİNALİ1 , Hasan Basri ULAŞ2 , Halil DEMIR 3

In this study, machinability tests were carried out using the newly produced TOOLOX 44 hot work tool steel (44 HRC) for use in the developing manufacturing sector. In machinability tests, the surface roughness of the work piece surface, the cutting force generated during the test, and the tool wear on the cutting tool were investigated according to the amount of chips removed. The tests were carried out dry through surface milling method at four different cutting speeds (150, 180, 210 and 240m/min), four different feed rates (0.4, 0.8, 1.2 and 1.6mm/tooth) and at two different depth of cut (0.2 and 0.4mm). In the abrasion tests, investigations were carried out according to the raised chip volume (320-1600-3200-6400mm3). As a result, the surface roughness value increased with the amount of feed rate and cutting speed, and the cutting force values decreased with the increase of the cutting speed depending on the amount of feed rate.

Keywords
TOOLOX 44, Surface Roughness, Tool Wear, Amount of Chip, Wear,

Details
   

Authors

Rüstem BİNALİ (1)

Selçuk Üniversitesi
rstmbinali@gmail.com | 0000-0003-0775-3817

Hasan Basri ULAŞ (2)

Gazi Üniversitesi
bulas@gazi.edu.tr | 0000-0002-9754-6055

Halil DEMIR (3) (Corresponding Author)
Karabük Üniversitesi
hdemir@karabuk.edu.tr | 0000-0002-9802-083X

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Daghini, L. and Nicolescu, C., (2007). Influence of Inserts Coating and Substrate on Toolox 44 Machining. Swedish Production Symposium.