• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-2109-4194
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0165
  • Page Number : 20-26
  • Doi : 10.12739/NWSA.2019.14.1.2A0165
  • Abstract Reading : 514
  • Download : 121
  • Share :

  • PDF Download

Issue Details

  • Year : 2019
  • Volume : 14
  • Issue : 1
  • Number of Articles Published : 4
  • Published Date : 1.01.2019

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

HASSAS DÖKÜM YÖNTEMİ İLE ÜRETİLEN ALAŞIMLARIN MİKROYAPI VE SERTLİK ÖZELLİKLERİNİN ARAŞTIRILMASI

Mustafa TÜRKMEN1 , Gizem ERDOĞAN2 , Ayşe Nur KAYA3

Bu çalışmada, metalik biyomalzemeler grubundan yüksek mekanik ve biyouyumluluk özellikleri ile dikkat çeken alaşımlardan; Ti6Al4V alaşımı ve 316L paslanmaz çelik malzemelerin hassas döküm yönetim ile üretilebilirliği üzerine çalışılmıştır. Deneysel çalışmalar, hassas döküm yöntemi ile Ti6Al4V ve 316L alaşımlarının üretilebileceğini göstermiştir. Mikroyapıya bağlı olarak, sertlik değerleri geliştirilebilen ve kontrol edilebilen özelliklerin önemli bir aşamasını oluşturmaktadır. Bu amaçla hassas döküm yöntemi ile üretimi gerçekleştirilen Ti6Al4V alaşımı ve 316 L paslanmaz çelik malzemelerin mikroyapı ve sertlik özellikleri irdelenmiştir.

Keywords
Hassas Döküm, Mikroyapı, Sertlik, Alaşım, Metal,

THE INVESTIGATION OF MICROSTRUCTURE AND HARDNESS PROPERTIES OF ALLOYS PRODUCED BY INVESTMENT CASTING METHOD

Mustafa TÜRKMEN1 , Gizem ERDOĞAN2 , Ayşe Nur KAYA3

In this study, reducibility of Ti6Al4V alloy and 316L stainless steel materials which are from the group of metallic biomaterials with their high mechanical and biocompatibility properties by investment casting method were investigated. Experimental studies showed Ti6Al4V and 316L alloys can be produced by investment casting method. Depending on the microstructure, hardness values constitute an important step of the properties that can be developed and controlled. To this end, Microstructure and hardness properties of Ti6Al4V alloy and 316L stainless steel materials produced by investment casting method were investigated.

Keywords
Investment Casting, Microstructure, Hardness, Alloy, Metal,

Details
   

Authors

Mustafa TÜRKMEN (1) (Corresponding Author)
Kocaeli Üniversitesi
mustafa.turkmen@kocaeli.edu.tr | 0000-0002-9402-2459

Gizem ERDOĞAN (2)

gzemerdogan_@hotmail.com | 0000-0000-0000-0058

Ayşe Nur KAYA (3)

aysenurkaya07_@hotmail.com | 0000-0002-2131-440X

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Beeley, P., (2001). Foundry Technology, Second Edition, Butter worth Heinemann, Oxford.