• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-7943-4246
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0111
  • Page Number : 43-52
  • Doi : 10.12739/NWSA.2017.12.2.2A0111
  • Abstract Reading : 530
  • Download : 118
  • Share :

  • PDF Download

Issue Details

  • Year : 2017
  • Volume : 12
  • Issue : 2
  • Number of Articles Published : 4
  • Published Date : 1.04.2017

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

TOZ METALURJİSİ İLE ÜRETİLEN Cu-FeB KOMPOZİT MALZEMELERİN MİKROYAPI VE ELEKTRİKSEL ÖZELLİKLERİNİN İNCELENMESİ

Aytekin ULUTAŞ1 , Hüseyin TURHAN 2

Bu çalışmada Toz Metalurjisi yöntemi ile Bakır Matrisli Kompozit içerisine, Ferrobor partikülleri takviye edilerek hazırlanan metal matrisli kompozitin, elektrik özellikleri inceleme altına alınmıştır. Bu amaçla Ferrobor takviye partikülü miktarı, yapı içinde ağırlıkça %1-1, 5-2-2, 5-3-3, 5 oranlarında seçilerek hazırlanan numuneler, toz metalürjisi yöntemi ile preslenmişlerdir. Ardından numunelere sinterleme işlemi için 800-850-900ºC sıcaklıklar uygulanarak, farklı sinterleme sıcaklıklarının kompozit özelliklerine etkisi incelenmiştir. Ayrıca MMC numunelerine iletkenlik deneyleri uygulanmıştır. Numunelerin mikroyapı karakterizasyonu ile SEM, EDS analizleri sonucunda, farklı sıcaklıklarda uygulanan sinterleme işlemi ile sinterleme sıcaklığı artışının numunelerin iletkenlik özelliklerini değiştirmediği görülmüştür. Farklı bileşim oranları dikkate alındığında, yapı içerisinde artan takviye partikülü oranına paralel olarak elektrik iletkenliği değerlerinin %2.5 Ferrobor takviye partikülü oranına kadar değişmediği, bu noktadan sonra yapı içerisinde bir miktar direnç artışı gözlendiği kaydedilmiştir.

Keywords
Toz Metalurjisi, Metal Matrisli Kompozit, Elektriksel Özellikler,, Cu , FeB ,

INVESTIGATION OF MICROSTRUCTURE AND ELECTRICAL CHARACTERISTICS OF Cu-FeB COMPOSITE MATERIALS PRODUCED BY POWDER METALLURGY

Aytekin ULUTAŞ1 , Hüseyin TURHAN 2

In this study, mechanical properties of ferroboron reinforced copper composite which produced by the powder metallurgy technique were studied. For this purpose, the ferroboron reinforced particles were mixed into copper powders in the rate of 1-1.5-2- 2.5-3-3.5% in weight. Then sintering to the sample with 800-850-900ºC temperatures, it is studied how different temperatures, effect the composites features. In addition, it was applied the conductivity test to the MMC sample. As the result of SEM EDS analysises with microstructure characterization it has been seen that the increase of sintering temperature doesn’t change their conductivities. Elektric conductivity volue doesn’t change till %2.5 Ferroboron consolidation particle rate after this point, it has been recorded that some resistance rise is seen in the structure.

Keywords
Powder Metallurgy , Metal Matrix Composite, Electrical Properties, Cu , FeB,

Details
   

Authors

Aytekin ULUTAŞ (1) (Corresponding Author)
Balıkesir Üniversitesi
aulutas@ba[INJ]sir.edu.tr | 0000-0002-5230-7122

Hüseyin TURHAN (2)

Fırat Üniversitesi
hturhan@firat.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Bolay, K.A., (1998). Microstructural Study of Hot Pressed PM Aluminum-Copper and Aluminum Copper Siliconcarbide Composites, M. Sc. Thesis, METU, Ankara.