• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8108-3705
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0380
  • Page Number : 123-132
  • Doi : 10.12739/NWSA.2017.12.2.1A0380
  • Abstract Reading : 648
  • Download : 142
  • Share :

  • PDF Download

Issue Details

  • Year : 2017
  • Volume : 12
  • Issue : 2
  • Number of Articles Published : 4
  • Published Date : 1.04.2017

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

ETİLEN GLİKOL+SÜLFÜRİK ASİT İÇERİSİNDE 7075 ALUMİNYUM ALAŞIMI ÜZERİNDE ALUMİNYUM OKSİT TABAKASININ GELİŞTİRİLMESİ

Sevgi ATEŞ1 , Rasiha Nefise Mutlu 2 , BAŞAK DOĞRU MERT3 , BIRGÜL YAZICI4

Bu çalışmada, 7075 aluminyum (Al) alaşımının korozyon dayanımının arttırılması amacıyla, Al yüzeyindeki oksit tabakasının geliştirilmesi hedeflenmiştir. 7075Al?un anot, Pt katot ve Ag/AgCl?nin referans elektrot olarak kullanıldığı üç elektrot sisteminde, 30 dakika boyunca farklı potansiyeller (0.5-2V) uygulanarak oluşan akımın, zamanla değişimleri belirlenmiştir. Elektrolit derişim etkisinin belirlenmesi için; değişik derişimde Etilen Glikol (EG) içeren (0.0; 0.1; 0.5; 0.6; 0.7; 1.0; 1.5 M), 0.4 M H2SO4 çözeltileri kullanılmıştır. Korozyon davranışları ise %3.5 NaCl içerisinde elektrokimyasal impedans spektroskopisi, akım-potansiyel eğrileri yardımıyla araştırılmıştır. Elde edilen bulgulara göre; en uygun oksit kaplama potansiyeli 2V, katkı derişimi 0,5M Etilen Glikol (EG)„dur. Bu koşullarda oluşturulan oksit tabakasının korozyon direnci, 0.4M H2SO4?de elde edilene göre yaklaşık iki kat artmıştır.

Keywords
7075 Aluminyum, Etilen Glikol , Korozyon, Gözenekli Oksit Filmi, Elektrokimyasal İmpedans Spektroskopisi,

THE DEVELOPMENT OF THE ALUMINUM OXIDE LAYER ON 7075 ALUMINUM ALLOY IN ETHYLENE GLYCOL+SULFURIC ACID

Sevgi ATEŞ1 , Rasiha Nefise Mutlu 2 , BAŞAK DOĞRU MERT3 , BIRGÜL YAZICI4

In this study,we aimed to develop oxide layer on 7075 aluminum alloy (Al) in order to increase the corrosion resistance of Al. A conventional three-electrode system, which 7075Al is anode, a platinum sheet is cathode and Ag/AgCl (3M KCl) is reference electrode was used under atmospheric condition, at different potentials (0.5-2V) during 30 minutes. The current-time curves were obtained. Due to determine the effect of additive concentrations (0.0; 0.1; 0.5; 0.6; 0.7; 1.0; 1.5M) Ethylene Glycol (EG) containing in 0.4 M H2SO4 were used. The corrosion behavior was investigated in 3.5% NaCl by electrochemical impedance spectroscopy,current-potential curves. The results showed that; the convenient potential is 2 V and the most suitable EG c oncentration is 0.5 M T he corrosion resistance of the oxide layer formed in this condition was increased about twice time compared to that obtained from 0.4 M H2SO4.

Keywords
7075 Aluminum, Ethylene Glycol, Corrosion, Porous Oxide Film, Electrochemical Impedance Spectroscopy,

Details
   

Authors

Sevgi ATEŞ (1) (Corresponding Author)
Kilis 7 Aralık Üniversitesi
sevgiiatess@gmail.com | 0000-0002-9502-6961

Rasiha Nefise Mutlu (2)

esifen@gmail.com

BAŞAK DOĞRU MERT (3)

bdogru@cu.edu.tr | 0000-0003-4809-7596

BIRGÜL YAZICI (4)

byazici@cu.edu.tr | 0000-0002-6175-192X

Supporting Institution

 :

Project Number

 :

Thanks

 :
References