• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

  • Article Code : FIRAT-AKADEMI-8456-3961
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0451
  • Page Number : 69-78
  • Doi : 10.12739/NWSA.2020.15.2.1A0451
  • Abstract Reading : 580
  • Download : 172
  • Share :

  • PDF Download

Issue Details

  • Year : 2020
  • Volume : 15
  • Issue : 2
  • Number of Articles Published : 5
  • Published Date : 1.04.2020

Cover Download Context Page Download
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

POLİETİLEN/SODYUM KAZEİNAT KARIŞIMLARINDAN EKSTRÜZYON YÖNTEMİYLE BİYOBOZUNUR FİLM ELDESİ, KARAKTERİZASYONU VE PLASTİKLEŞTİRİCİ ETKİSİNİN İNCELENMESİ

Hülya Sema KÖKER1 , HÜLYA YAVUZ ERSAN2 , AYŞE AYTAÇ3

Bu çalışmada, polietilen(PE)/sodyum kazeinat(NaCAS) karışımlarından ekstrüzyon yöntemi kullanılarak film üretimi gerçekleştirilmiştir. Mekanik test sonuçlarına göre PE ile ağırlıkça %5 ve %15 NaCAS kullanılmıştır. Plastikleştirici olarak gliserol(GLY) 0.5, 1.0, 1.5 ve 2.0 oranlarında (GLY/NaCAS-g/g) eklenmiştir. Karışımlar ekstrüderde 135°C, 100 rpm ve 3 dakika boyunca harmanlanarak pelet haline getirilmiştir ve sonrasında basınçlı kalıplama ile film üretilmiştir. Filmlerin; mekanik, ısıl, temas açısı, su buharı geçirgenliği gibi özellikleri belirlenmiştir. Fourier dönüşümlü kızılötesi spektroskopisi (FTIR) ve taramalı elektron mikroskobu (SEM) analizleri ile karakterizasyon testleri gerçekleştirilmiştir. NaCAS oranı arttıkça çekme dayanımı azalmıştır, GLY oranı arttıkça çekme dayanımı artmıştır. Kopmada uzama, 5NaCAS/PE’de artan GLY oranlarında artarken, 15NaCAS/PE de 0.5GLY oranı hariç düşmüştür. Erime sıcaklığı PE içerisine eklenen NACAS ile azalmış, artan GLY oranında anlamlı bir değişiklik yaratmamıştır. Temas açısı, artan NACAS ve GLY oranı ile azalmıştır. Su buharı geçirgenliği artan NaCAS oranında artmış ve 1GLY oranında daha da artmıştır. SEM görüntülerinde, 5NACAS/PE-1GLY oranında homojen yapının oluştuğu, 15NaCAS/PE-1GLY oranında ise homojen yapının bozulduğu gözlenmiştir.

Keywords
Biyobozunur Film, Ekstrüzyon, Polietilen, Plastikleştirici, Sodyum Kazeinat ,

PRODUCTION AND CHARACTERIZATION OF POLYETHYLENE/SODIUM CASEINATE BIODEGRADABLE FILMS OBTAINED BY EXTRUSION AND INVESTIGATION OF THE EFFECT OF PLASTICIZER

Hülya Sema KÖKER1 , HÜLYA YAVUZ ERSAN2 , AYŞE AYTAÇ3

In this study, the films were produced from polyethylene/sodium caseinate mixtures by extrusion. 5% and 15% by weight NaCAS were used according to mechanical test results. Glycerol, selected as plasticizer, used as 0.5, 1.0, 1.5 and 2.0 GLY/NaCAS-g/g. The films were produced at 135°C, 100rpm and for 3 minutes as pellets by extrusion followed by a heat press. The mechanical, thermal, contact angle, water vapor permeability, FTIR and SEM tests were performed. It was observed that the tensile strength decreased with increasing NaCAS, increased with increasing GLY. The elongation at break increased with increasing GLY in 5NaCAS/PE but, decreased in 15NaCAS/PE films except 0.5 of GLY. The melting temperature decreased with increasing NaCAS and no significant change observed with increasing GLY. The contact angle decreased with increasing NaCAS and GLY. WVP increased with increasing NaCAS and further increased at 1GLY ratio. 5NaCAS/PE-1GLY and 15NaCAS/PE-1GLY films indicated homogenous and non-homogenous structures in the SEM images, respectively.

Keywords
Biodegradable Film, Extrusion, Plasticizer, Polyethylene, Sodium Caseinate,

Details
   

Authors

Hülya Sema KÖKER (1) (Corresponding Author)

HACETTEPE UNIVERSITY
hulyasemak@gmail.com | 0000-0002-7890-4259

HÜLYA YAVUZ ERSAN (2)

Hacettepe Üniversitesi
hyavuz@hacettepe.edu.tr | 0000-0002-5587-275X

AYŞE AYTAÇ (3)

Kocaeli üniversitesi
aaytac@gmail.com | 0000-0002-9566-7881

Supporting Institution

:

Project Number

:

Thanks

:
References
[1] Pan, Y., Farmahini-Farahani, M., O’Hearn, P., Xiao, H., and Ocampo, H., (2016). An Overview of Bio-based Polymers for Packaging Materials. Journal of Bioresources and Bioproducts, 1(3):106-113.