• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8531-4003
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0414
  • Page Number : 217-228
  • Doi : 10.12739/NWSA.2018.13.3.1A0414
  • Abstract Reading : 606
  • Download : 149
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 3
  • Number of Articles Published : 9
  • Published Date : 1.07.2018

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

TRIP VE DP ÇELİKLERİNDE DİRENÇ NOKTA KAYNAĞI PARAMETRELERİNİN MEKANİK ÖZELLİKLERE ETKİSİ

Yunus Emre ANTİKA1 , ZAFER TATLI2 , FATIH ÇALIŞKAN3

Otomotiv sektöründe kullanılan Gelişmiş Yüksek Mukavemetli Çelik (AHSS) türlerinden yaygın olarak kullanılan TRIP ve DP çelikleri Direnç Nokta Kaynağı ile kaynatılarak mekanik özellikleri ve mikroyapıları incelenmiştir. Bu amaca yönelik olarak 1mm DP1000 ve 1.5mm TRIP800 levhaların faklı kaynak akımı ve kaynak sürelerinde kaynatılmıştır. Bu işlemden sonra çekme makaslama, mekanize soyma testleri ve sertlik ölçümleri yapılmıştır. Esas metal ve kaynak bölgesi faz analizi için SEM çalışmaları yapılmıştır. Kaynakların çekirdek bölgelerindeki martenzit yoğunluğunun arttığı görülmüştür. Elde edilen sonuçlar mekanize soyma ve çekme makaslama dayanımlarının, artan kaynak akımı ve kaynak süresine bağlı olarak arttığını ayrıca kaynak çekirdeğinin sertlik değerinin de esas metale göre yaklaşık %70 arttığını ortaya koymuştur.

Keywords
DP ve TRIP çelikleri, Direnç Nokta Kaynağı, Gelişmiş Yüksek Mukavemetli Çelikler, Mikroyapı, Mekanik Özellikler,

EFFECT OF THE RESISTANCE SPOT WELDING PARAMETERS IN TRIP AND DP STEELS ON MECHANICAL PROPERTIES

Yunus Emre ANTİKA1 , ZAFER TATLI2 , FATIH ÇALIŞKAN3

Advanced High Strength Steels (AHSS) such as TRIP and DP steels are commonly used in the automotive industry were welded with Resistance Spot Welding and their mechanical and microstructural properties were investigated. For this purpose, 1mm DP1000 and 1.5mm TRIP800 plates were welded at different welding currents and welding times. After welding, tensile shear, mechanized peeling tests and hardness measurements of welded plates were investigated. SEM studies and phase analysis were carried out of the main metal and weld zone. The results showed that the strength of the mechanized peeling and tensile shear strength increased with increasing welding current and welding time. Hardness of the weld nuggets were increased about 70% compared to the main metal with increasing welding current and welding time as well.

Keywords
DP and TRIP Steels, Resistance Spot Welding, Advanced High Strength Steel (AHSS), Microstructure, Mechanical Properties,

Details
   

Authors

Yunus Emre ANTİKA (1) (Corresponding Author)
SAKARYA UYGULAMA BILIMLER ÜNIVERSITESI
yunusemreantika@hotmail.com | 0000-0002-0675-5354

ZAFER TATLI (2)

ztatli@subu.edu.tr | 0000-0001-5617-3064

FATIH ÇALIŞKAN (3)

fcaliskan@subu.edu.tr | 0000-0002-9568-7049

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Keeler, S., Kimchi, M., and Mooney., P.J., (2017). Advanced High-Strength Steels Apllication Guidelines Version 6.0.