• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8574-4033
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0379
  • Page Number : 117-122
  • Doi : 10.12739/NWSA.2017.12.2.1A0379
  • Abstract Reading : 535
  • Download : 111
  • Share :

  • PDF Download

Issue Details

  • Year : 2017
  • Volume : 12
  • Issue : 2
  • Number of Articles Published : 4
  • Published Date : 1.04.2017

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

PLAZMA OKSİDASYON İŞLEMİNİN AISI 316 PASLANMAZ ÇELİĞİNİN KOROZYON DAVRANIŞINA ETKİSİ

MEHMET KARAHAN1 , ABDULMUTTALIP YENILMEZ2 , İlhan Çelik3

Bu çalışmada, AISI 316 paslanmaz çelik numunelerin yüzeylerine iki farklı plazma oksidasyon işlemi uygulanmıştır. Plazma oksidasyon işlemlerinden biri sadece oksijen ortamında yapılırken (PO1) diğeri ise eşit oranda hidrojen ve oksijen gazlarının karışımından oluşan (PO2) plazma ortamında gerçekleştirilmiştir. Numunelerin korozyon davranışını tespit edebilmek için korozyon deneyleri yapılmıştır. Ayrıca işlemsiz ve yüzey işlemi uygulanmış numunelerin yapısal analizleri için SEM ve XRD cihazları kullanılmıştır. Yapılan plazma oksidasyon işlemlerinin ardından malzeme yüzeyinde ağırlıklı olarak manyetit fazının oluştuğu tespit edilmiştir. Ayrıca PO1 ve PO2 işlemlerinden sonra elde edilen yüzeylerin göstermiş oldukları korozyon davranışının, işlemsiz numunelerinkine yakın karakterde olduğu görülmüştür.

Keywords
AISI 316 Paslanmaz Çeliği, Plazma Oksidasyon, Korozyon, SEM, XRD,

INFLUENCE OF PLASMA OXIDATION ON CORROSION BEHAVIOR OF AISI 316 STAINLESS STEEL

MEHMET KARAHAN2 , ABDULMUTTALIP YENILMEZ3 , İlhan Çelik3

In this study, two different plasma oxidation treatments were applied on the surface of AISI 316 stainless steel specimens. One of the plasma oxidation treatments was applied in 100 % oxygen atmosphere (PO1) and the other was carried out in the equally composed of a mixture of hydrogen and oxygen (PO2) atmosphere. Corrosion tests were performed in order to determine the corrosion behavior of the sample. SEM and XRD devices were used for structural analysis of untreated and the plasma oxidized samples. It was determined to be mainly composed of magnetite phase on the surfaces of specimens after the plasma oxidation treatments. Also it was found that the corrosion behaviors of PO1 and PO2 applied surfaces were similar character with the untreated specimens.

Keywords
AISI 316 stainless steel, Plasma oxidation, Corrosion, SEM, XRD,

Details
   

Authors

MEHMET KARAHAN (1)

mkarakan@atauni.edu.tr | 0000-0000-0000-0040

ABDULMUTTALIP YENILMEZ (2)

ayenilmz2@gmail.com | 0000-0000-0000-0041

İlhan Çelik (3) (Corresponding Author)
Samsun Üniversitesi
ilhan.celik@samsun.edu.tr | 0000-0001-6757-834X

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] DeBerry, D.W., (1985). Modification of the Electrochemical and Corrosion Behavior of Stainless Steels with an Electroactive Coating, J. Electrochem. Soc., 132(5), 1022-1026.