• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8888-4217
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0139
  • Page Number : 89-97
  • Doi : 10.12739/NWSA.2018.13.2.2A0139
  • Abstract Reading : 495
  • Download : 107
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 2
  • Number of Articles Published : 14
  • Published Date : 1.04.2018

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

PA6/PTFE KARIŞIMLARININ TRİBOLOJİK PERFORMANSLARININ İNCELENMESİ

Salih Hakan YETGİN1 , Hüseyin Ünal2

Bu çalışmada önce, katkısız poliamid 6 ile ağırlık olarak %5 ve %10 oranlarında poly-tetra-flor-etilen (PTFE) katkılı poliamid 6 polimer karışımlarının aşınma ve sürtünme davranışları incelenmiştir. Polimer karışımları, endüstriyel tip ikiz vidalı bir kompound makinasında granül formda üretilmiştir. Deneylerde kullanılan test numuneleri geleneksel enjeksiyon makinası kullanılarak basılmıştır. Katkısız PA 6 ve PA 6 karışımlarının aşınma ve sürtünme davranışları pim-disk aşınma cihazında ve kuru kayma şartları altında gerçekleştirilmiştir. Katkısız PA 6 ve PA 6/PTFE karışımlarının aşınma ve sürtünme davranışları 0.5m/s kayma hızında ve 10N, 20N ve 30N yükler altında yapılmıştır. Çalışma sonucunda, PA 6 polimerine ilave edilen PTFE katkı, polimer karışımının hem sürtünme katsayısı hem de spesifik aşınma hızı değerlerinin azalmasına sebep olmuştur. Uygulanan yükün artması ile sürtünme katsayısı değerleri azalırken spesifik aşınma hızı değerleri de artmıştır.

Keywords
Poliamid 6, PTFE, Sürtünme, Aşınma, Polimer, Triboloji,

THE INVESTIGATION OF TRIBOLOGICAL PERFORMANCES OF PA6/PTFE BLENDS

Salih Hakan YETGİN1 , Hüseyin Ünal2

In this experimental study, the friction and wear behaviors of unfilled polyamide 6 (PA 6) polymer and different amount (5wt.%-10wt.%) of poly-tetra-fluoro-ethylene (PTFE) filled polyamide 6 polymer blends have been studied. Polymer blends as a granule form were prepared by compounding machine with a twin screw extruder. Friction and wear test samples were molded with an ordinary injection molding machine. Friction and wear studies were carried out using a pin-on-disc wear test rig under dry sliding conditions. Friction and wear tests were run at 0.5m/s sliding speed and under the applied loads of 10, 20 and 30N. The results show that the addition of PTFE powder into the polyamide 6 polymer resulted to decrease in coefficient of friction and specific wear rate values. In addition, the specific rate values increased with the increase in applied load from 10N to 30N but the coefficient of friction decreases with the increment of applied load value.

Keywords
Polyamide 6, PTFE, Friction, Wear, Polymer, Tribology,

Details
   

Authors

Salih Hakan YETGİN (1) (Corresponding Author)
Dumlupınar University
shyetgin@gmail.com | 0000-0002-6068-9204

Hüseyin Ünal (2)

unal@sakarya.edu.tr | 0000-0003-0521-6647

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Bolvari, S., Glenn, R.J., and Ellis, C., (1997). Wear and Friction of Aramide Fiber and Polytetrafluoroethylene Filled Composites, Wear, Volume:203-204, pp:697-702.