• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : NWSA-685-443
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0002
  • Page Number : 12-22
  • Doi : 10.12739/
  • Abstract Reading : 1312
  • Download : 143
  • Share :

  • PDF Download

Issue Details

  • Year : 2009
  • Volume : 4
  • Issue : 1
  • Number of Articles Published : 13
  • Published Date : 1.01.2009

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

DUAL-FAZ ISIL İŞLEMİ UYGULANMIŞ BETONARME ÇELİĞİNİN ÇEKME EĞRİSİNE TEMPERLEME ISIL İŞLEMİNİN ETKİSİ

Oğuzhan KELEŞTEMUR 1 , Servet YILDIZ 2

Bu çalışmasında, inşaat sektörünün temel yapı malzemesi olan ve yurdumuzda bol miktarda üretilen düşük karbonlu SAE1010 inşaat çeliğinden dual-faz çeliği üretilerek, elde edilen bu çeliğin kuvvet-uzama eğrisi üzerine temperleme ısıl işleminin etkisi incelenmiştir. İnşaat çeliğine, (α+γ) bölgesinde 20, 40 ve 60 dk süre ile ostenitleme yapıldıktan sonra buz+su karışımında su verilerek farklı martenzit hacim oranlarına sahip dual-faz çelikleri elde edilmiştir. Daha sonra bu dual-faz çelikleri 200, 300 ve 400 oC sıcaklıklarda 45 dk süre ile temperlenerek sakin havada soğutulmuştur. Elde edilen dual-faz çeliklerinin metalografik incelemeleri tamamlandıktan sonra, çekme deneyine tabi tutularak kuvvet-uzama eğrileri elde edilmiştir. Elde edilen bu eğriler yardımıyla numunelerin çekme dayanımı, akma dayanımı ve tokluk gibi mekanik özellikleri belirlenmiştir. Çalışma neticesinde, elde edilen dual-faz çeliklerinin çekme deneyi esnasında sabit akma noktası göstermediği belirlenmiştir. A

Keywords
İnşaat Çeliği, Dual-Faz Çeliği, Temperleme, Kuvvet-Uzama Eğrileri, ÇEKME DAYANIMI,

EFFECT OF TEMPERING HEAT TREATMENT ON THE TENSILE CURVE OF REINFORCED STEEL SUBJECTED TO DUAL-PHASE HEAT TREATMENT

Oğuzhan KELEŞTEMUR 1 , Servet YILDIZ 1

In this study, dual-phase steel by producing from SAE1010 structural carbon steel, which is the fundamental construction material of construction industry and wide range of product in our country, effect of tempering heat treatment on the tensile curve of this steel has been investigated. Dual-phase steel having different martensite volume ratio has been obtained by applying different quenching conditions; its (á+ã) structure, is immersed into the ice+water medium and then it is annealed for various duration; 20, 40 and 60 minutes. Additionally, these dual-phase steels have been tempered at 200, 300 and 400 oC for 45 minutes and then cooled to the room temperature. After the metallographic examination of the steels has been done, load-elongation curves of these steels have been obtained. The mechanical properties as tensile strength, yield strength and toughness have been determined with aid of load-elongation curves. It is observed that serrated flow behavior on the DP specimens i

Keywords
Reinforcing Steel, Dual-Phase Steel, Tempering, Load-Elongation Curves, TENSILE STRENGTH,

Details
   

Authors

Oğuzhan KELEŞTEMUR (1) (Corresponding Author)
Fırat Üniversitesi
okelestemur@firat.edu.tr

Servet YILDIZ (2)

Fırat Üniversitesi
syildiz@firat.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References