• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-7910-4257
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0105
  • Page Number : 171-184
  • Doi : 10.12739/NWSA.2016.11.4.2A0105
  • Abstract Reading : 714
  • Download : 144
  • Share :

  • PDF Download

Issue Details

  • Year : 2016
  • Volume : 11
  • Issue : 4
  • Number of Articles Published : 6
  • Published Date : 1.10.2016

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

PTA YÖNTEMİ İLE GERÇEKLEŞTİRİLEN FE-CR-W-B-C KOMPOZİT KAPLAMASININ MİKROYAPI VE MEKANİK ÖZELLİKLERİ

Turan GÜRGENÇ1 , Cihan ÖZEL2

Bu çalışmada, düşük karbonlu AISI 1020 çeliğinin yüzeyi Fe-Cr-W-B-C kompozit kaplamasıyla plazma transfer ark (PTA) kaynak yöntemi kullanılarak kaplanmıştır. Kaplama tozu olarak ağırlıkça yüzde 80FeCrC-10FeW-10FeB ve 60FeCrC-20FeW-20FeB karışımları kullanılmıştır. Kaplamalar iki farklı ilerleme hızı (0.15 m/dk, 0.1 m/dk) ve akım değerinde (120 A, 160 A) gerçekleştirilmiştir. Kaplama işleminden sonra kaplama tabaları OM, SEM ve EDS ile incelenmiştir. Kaplanan numuneler mikrosertlik testine ve pin-on-disk aşınma testine tabi tutulmuştur. Fe-Cr-W-B-C ile AISI 1020 çeliğinin yüzeyinin PTA yöntemi kullanılarak sorunsuz şekilde kaplanabildiği tespit edilmiştir. Maksimum mikrosertlik değeri 1668 Hv0.2 olarak ölçülmüştür. Fe-Cr-W-B-C ile yüzeyi kaplanmış AISI 1020’ nin aşınma direncinin ve sertliğinin kaplanmamış AISI 1020’ ye oranla daha yüksek olduğu tespit edilmiştir.

Keywords
PTA kaynağı, Fe-Cr-W-B-C Kaplama, Karbür,, Aşınma, Mikrosertlik,

MICROSTRUCTURAL AND WEAR PROPERTIES OF FE-CR-W-B-C COMPOSITE COATING PERFORMED WITH PTA METHOD

Turan GÜRGENÇ1 , Cihan ÖZEL2

In this study, surface of low carbon steel AISI 1020 was coated with Fe-Cr-W-B-C composite coating by using plasma transferred arc (PTA) welding method. For coating powders in chemical composition of (wt. %) 80FeCrC-10FeW-10FeB and 60FeCrC-20FeW-20FeB mixtures were used. The coatings were carried out at two different travelling speed (0.15 m/min.), 0.1 m/min.) and current (120 A, 160 A). After coating process, the coating layers was examined by OM, SEM and EDS. Coated samples were subjected to microhardness test and pin-on-disc wear test. It was determined that the AISI 1020 steels surface can be coated with Fe-Cr-W-B-C without any problems by using PTA method. The maximum microhardness was measured 1668 Hv0.2. It was determined that the wear resistance and microhardness of the coated AISI 1020 surface with Fe-Cr-W-B-C was higher than the uncoated AISI 1020.

Keywords
PTA welding, Fe-Cr-W-B-C Coating, Carbide, Wear, Microhardness,

Details
   

Authors

Turan GÜRGENÇ (1) (Corresponding Author)
Fırat Üniversitesi
tgurgenc@gmail.com | 0000-0002-7678-2673

Cihan ÖZEL (2)

cozel@firat.edu.tr | 0000-0002-3227-6875

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Cheng, J.B., Xu, B.S., Liang, X.B., and Wu, Y.X., (2008). Microstructure and Mechanical Characteristics of Iron-Based Coating Prepared by Plasma Transferred Arc Cladding Process. Materials Science and Engineering: A. Cilt:492, Sayı:1, ss:407-412.