• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-7945-4247
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0110
  • Page Number : 38-42
  • Doi : 10.12739/NWSA.2017.12.2.2A0110
  • Abstract Reading : 634
  • Download : 140
  • Share :

  • PDF Download

Issue Details

  • Year : 2017
  • Volume : 12
  • Issue : 2
  • Number of Articles Published : 4
  • Published Date : 1.04.2017

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

YAPAY AĞIZ SIVISINDA TERMAL ÇEVRİMİN KOMPOZİT RESTORATİF MALZEMELERİNİN YÜZEY PÜRÜZLÜLÜĞÜ ÜZERİNDEKİ ETKİSİ

Efe Çetin YILMAZ1 , Recep SADELER2

Bu çalışmanın amacı korozif yapay ağız sıvısı ortamında termal çevrimin iki farklı restoratif kompozit diş dolgu malzemelerinin yüzey pürüzlülüğü(Ra) üzerindeki etkisinin incelenmesidir. Bu çalışmada Renamel Microfill ve Kuraray Clearfil AP-X kompozit diş dolgu malzemelerinden üretici firmanın önerdiği ortam koşullarında 4 mm X 8 mm (yükseklik X çap) boyutunda 8 adet üretildi.(n=8) Üretilen numuneler korozif ağız sıvısı (0.4 NaCI + .4 KCI + 0.795 CaCl2.2H2O + 0.005 Na2S.9H2O + 0.69 NaH2PO4.2H2O + 1 Urea (gram/litre)) ortamında 5°C ve 55°C sıcaklıklar arasında kontrol grup, 3000 ve 6000 termal çevrim testlerine maruz bırakıldı. Bu testler sonucunda elde edilen veriler ANOVA ve TUKEY testlerine tabi tutuldu ve anlamlılık düzeyleri yorumlandı (?<0.005). Her iki malzemede de bu testler sonucunda yüzey pürüzlülük değerlerinde (Ra) artış olduğu görülmüştür. Elde edilen bu bulgular kompozit malzemenin sahip olduğu organik matriks yapısı TEGDMA (Triethylene glycol dimethacrylate) yapısının korozif ortamda termal çevrim testlerinden daha çok etkilendiğini ortaya koymuştur.

Keywords
Restoratif Kompozit Malzeme, Termal Çevrim, Yüzey Pürüzlülüğü, Yapay Tükürük Sıvısı, SEM,

EFFECT OF THERMAL CYCLING ON SURFACE OF ROUGHNESS COMPOSITE RESTORATIVE MATERIALS IN ARTIFICAL SALIVA

Efe Çetin YILMAZ1 , Recep SADELER2

The purpose of this study effect of thermal cycles on surface of roughness of different composite restorative materials in corrosive artificial saliva environment. In this study Renamel Microfill and Kuraray Clearfil AP-X composite restorative specimens (6mm diameter and 5mm height) consisting of 8 specimens for each material (n=8) were prepared following the manufacturer’s instructions. Produced samples were subjected variable temperature between 5°C and 55°C control group, 3000 and 6000 thermal cycle procedure in corrosive artifical saliva (0.4 NaCI + 0.4 KCI + 0.795 CaCl2.2H2O + 0.005 Na2S.9H2O + 0.69 NaH2PO4.2H2O + 1 Urea (gram/liter). The data obtained in these tests were subjected to ANOVA and Tukey's tests. (?<0.005). Both Renamel Microfill and Kuraray Clearfil AP-X have increased surface of roughness value (Ra) after tests. The composition of material, including the type of organic matrix TEGDMA (Triethylene glycol dimethacrylate) could be more relevant to roughness maintenance over time than the general behavior of composites based on particle fillers.

Keywords
Composite Restorative Material, Thermal Cycle, Surface of Roughness, Artificial Saliva, SEM,

Details
   

Authors

Efe Çetin YILMAZ (1) (Corresponding Author)
Atatürk Üniversitesi
efecetinyilmaz@msn.com | 0000-0000-0000-0061

Recep SADELER (2)

receps@atauni.edu.tr | 0000-0001-5380-9733

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Dos Santos, P.H., et al., (2015). Effect of Thermocycling on Roughness of Nanofill, Microfill and Microhybrid Composites. Acta Odontologica Scandinavica, 73(3), pp:176-181.