• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8089-4026
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0384
  • Page Number : 158-167
  • Doi : 10.12739/NWSA.2017.12.3.1A0384
  • Abstract Reading : 691
  • Download : 162
  • Share :

  • PDF Download

Issue Details

  • Year : 2017
  • Volume : 12
  • Issue : 3
  • Number of Articles Published : 6
  • Published Date : 1.07.2017

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

FOSFAT VE SİLİKAT KAPLANMIŞ ÇİNKONUN KOROZYONUNA ANİLİN VE Ce+3’ÜN ETKİSİ

DERYA ALTUĞ1 , TURAN YANARDAĞ2 , ALI ABBAS AKSÜT3

Bu çalışmada, fosfat (disodyum fosfat, SP) ve silikat (disodyum silikat, SS) iyonları ile ön işlem yapılmış saf çinkonun klorür ortamındaki korozyonuna anilin ve Ce3+’ün etkisi araştırılmıştır. Fosfat ve silikat kaplanmış çinko, Ce3+ ile etkileştirilip ve oksalat+anilin çözeltisinde dönüşümlü voltametri alındıktan sonra sodyum klorür ortamındaki korozyonu potansiyelin zamanla değişimi (OCP), AC-empedans (EIS) ve akım-potansiyel eğrileri alınarak incelenmiştir. Silikat üzerine yüksek derişimli seryum kaplama çinkonun korozyon hızının daha düşük olduğunu ve çinko metalini korozyondan daha fazla koruduğunu (%99) göstermiştir.

Keywords
Korozyon, Çinko, Seryum, Silikat, Anilin,

THE EFFECT OF ANILIN AND Ce+3 ION ON THE CORROSION OF CATED ZINC WITH PHOSPHATE AND SILICATE

DERYA ALTUĞ1 , TURAN YANARDAĞ2 , ALI ABBAS AKSÜT3

In this study, the effects of anilin and Ce3+ ions was investigeted with pre-treatment phosphate (disodyum phosphate, SP)and silicate (disodyum silikat, SS) ions on zinc. On the zinc sufrace pre-treatment with phosphate and silicate ions interacted with Ce3+ and after optained cyclic voltametry in ox+aniline solution was researched zinc electrode corrosion by potential changes with time (OCP), AC-impedance (EIS) and current-potentail curves in sodium cloride solution. It was shown that coated with higher concentration of Ce3+ on silicate exhibited lower corrosion rate and provided better corrosion protection (99%) on zinc.

Keywords
Corrosion, Zinc, Cerium, Silicate, Aniline ,

Details
   

Authors

DERYA ALTUĞ (1)

deryaaltug92@gmail.com | 0000-0002-9036-9500

TURAN YANARDAĞ (2) (Corresponding Author)
Ankara Üniversitesi
tyanardag@ankara.edu.tr | 0000-0001-7292-0891

ALI ABBAS AKSÜT (3)

aksut@science.ankara.edu.tr | 0000-0003-3076-4282

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Tallman, D.E., Spinks, G., Dominis, A., and Wallace, G.G., (2002). Electroactive Conducting Polymers for Corrosion Control. Part 1. General Introduction and A Review of Non-Ferrous Metals, Journal of Solid State Electrochemistry, Volume:6, pp:73-84.