• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8485-3984
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0427
  • Page Number : 17-25
  • Doi : 10.12739/NWSA.2019.14.1.1A0427
  • Abstract Reading : 777
  • Download : 170
  • Share :

  • PDF Download

Issue Details

  • Year : 2019
  • Volume : 14
  • Issue : 1
  • Number of Articles Published : 5
  • Published Date : 1.01.2019

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

ZİRKONYUM KARBÜR ESASLI AŞIRI YÜKSEK SICAKLIK SERAMİK KOMPOZİT TOZLARIN METALOTERMİK YÖNTEMLE ÜRETİMİ

Ahmet ATASOY1 , BÜŞRA DEMIR2

Günümüzde malzeme bilimi çok gelişmiş olmasına rağmen, yeni teknolojik gereksinimler, var olanlardan farklı yeni nesil malzemelere ihtiyaç duyulmaktadır. Yakın bir gelecekte uzay yolculuğunun gerçekleşebilir olması; aşırı yüksek sıcaklık ortamlarında, çok amaçlı ve tekrarlı kullanılabilir seramik kompozit malzemelerin geliştirilmesine bağlıdır. Aşırı yüksek sıcaklık seramik malzemeleri (AYSS veya Ultra high temperature ceramics-UHTC) 2300°C ve üzerindeki ortamlarda kullanılabilir seramikler olarak tanımlanmaktadır. Bu çalışmada, yüksek ergime noktasına sahip, kimyasal ve termal kararlılığı olan AYSS grubuna ait, ZrB2-ZrC- SiC-Al2O3 seramik kompozit tozlarının üretimi, laboratuvar şartlarında, zirkon, borik asit, metalik alüminyum ve grafit başlangıç karışımı kullanılarak araştırılmıştır. Alüminotermik yöntem kullanılmış, başlangıç karışımları ve elde edilen reaksiyon ürünleri SEM, XRD, XRF, TG/DTA gibi analiz yöntemleri ile analiz edilmiştir. Deneysel şartlara bağlı olarak, başlangıç karışımında bulunan zirkon, çok düşük sıcaklıklarda ayrışmıştır. Zirkonyum ve silisyum oksitleri, ZrC ve ZrB2 ve SiC fazına dönüştüğü görülmüştür. Karbür ve borür fazlarının haricinde, proses edilmiş numunelerde Al2O3 oluşumu da tespit edilmiştir.

Keywords
Zirkon, Zirkonyum Borür, Karbür, Alümina, Seramik,

PRODUCTION OF ZRC BASED ULTRA HIGH TEMPERATURE CERAMIC COMPOSITE POWDERS BY METALLOTHERMIC METHOD

Ahmet ATASOY1 , BÜŞRA DEMIR2

Although material science is advanced at present time, new technological developments require new generation and different materials that are commercially not available in global market. In order to make long distance space journeys possible in near future, innovation of multipurpose and reusable ceramic composite materials for at high temperature environments are needed. Ceramics that are useable at elevated temperatures as high as 2300°C are called Ultra high temperature ceramics (UHTC). In this study, the processing of UHTCs based on ZrC/ZrB2/SiC/Al2O3 ceramic composite that has high melting point, chemical and thermal stability, at the laboratory conditions was investigated using zircon, boric acid, carbon and aluminium powders. Aluminothermic method was chosen, the starting mixtures and the obtained reaction products were analysed using SEM, XRD, XRF and TG/DTA analysis methods. The experimental results showed that, the obtained sample consists of ZrB2/ZrC as a matrix phases.

Keywords
Zircon, Zirconium Diboride, Carbide, Alumina, Ceramic,

Details
   

Authors

Ahmet ATASOY (1) (Corresponding Author)
SAKARYA UYGULAMALI BILIMLER ÜNIVERSITESI
aatasoy@subu.edu.tr | 0000-0003-1564-8793

BÜŞRA DEMIR (2)

dmrbsr43@gmail.com | 0000-0002-8904-8742

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Fahrenholtz, W.G., Hilmas, G.E., Talmy, I.G., and Zaykoski, J.A., (2007). Refractory Diborides of Zirconium and Hafnium, J American Ceramic Society. Cilt:90, No:5, ss:1347-1364.