Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-879-4259
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0095
  • Page Number : 75-85
  • Doi : 10.12739/NWSA.2016.11.3.2A0095
  • Abstract Reading : 697
  • Download : 156
  • Share :

  • PDF Download

Issue Details

  • Year : 2016
  • Volume : 11
  • Issue : 3
  • Number of Articles Published : 3
  • Published Date : 1.07.2016

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

TRD YÖNTEMİYLE SUPAP ÇELİĞİ YÜZEYİNDE ÜRETİLEN KAPLAMALARIN MİKROYAPI VE AŞINMA ÖZELLİKLERİ

Serkan ISLAK1 , Cihan ÖZORAK2 , Cihangir Tevfik SEZGİN3 , Mehmet AKKAŞ4

Bu çalışmada, kullanım yeri itibariyle sürekli aşınmaya maruz kalan supapların Termoreaktif Difüzyon (TRD) tekniği kullanılarak karışık nitrür esaslı kaplamalarla ile kaplanması ve mikroyapı özelliklerinin incelenmesi gerçekleştirilmiştir. Bu amaçla, supap yüzeyine önce nitrürasyon işlemi uygulanmıştır ve sonra TRD yöntemiyle supap yüzeyine bor geçiştirilmiştir. Üretilen kaplamaların mikroyapı ve faz bileşimi incelemesi, taramalı elektron mikroskobu (SEM), X-ışın difraktogramı (XRD), X ışını enerji dağılım spektrometresi (EDS) ile yapılmıştır. Kaplamaların sertlikleri vikers olarak ölçülmüştür. Kaplamaların aşınma davranışı, tüm numunelere aynı koşullarda uygulanan ball on disk aşınma testleri yapılarak karşılaştırılmıştır. Kaplamaların sürtünme katsayıları nispeten düşük çıkmıştır.

Keywords
TRD, Kaplama, Supap, Mikroyapı, Aşınma,

MICROSTRUCTURE AND WEAR PROPERTIES OF COATINGS ON VALVE STEEL PRODUCED BY TRD METHOD

Serkan ISLAK1 , Cihan ÖZORAK2 , Cihangir Tevfik SEZGİN3 , Mehmet AKKAŞ4

In this study, coating with mix nitride based coating of valves, subjected to constant wear, by thermo-reactive diffusion (TRD) technique and examination of their microstructural features were carried out. For this purpose, firstly the nitriding process was applied to the valve surface and then boron deposited to valve surface by TRD method. Phase compound and microstructure of coatings were examined using scanning electron microscope (SEM), X-ray diffractometer (XRD) and X-ray energy dispersive spectrometer (EDS). The hardness was measured as Vickers. The wear behavior of the coatings was compared with ball-on-disc configuration wear tests, at the same conditions. Average coefficient of friction values of the coatings were obtained at relatively low levels.

Keywords
TRD, Coating, Valve, Microstructure, Wear,

Details
   

Authors

Serkan ISLAK (1) (Corresponding Author)
Kastamonu Üniversitesi
serkanislak@gmail.com | 0000-0001-9140-6476

Cihan ÖZORAK (2)

ozorak@kastamonu.edu.tr | 0000-0003-3052-3024

Cihangir Tevfik SEZGİN (3)

Welding Technologies
ctsezgin@kastamonu.edu.tr | 0000-0001-9786-6895

Mehmet AKKAŞ (4)

Kastamonu University
mehmetakkas@kastamonu.edu.tr | 0000-0000-0000-0101

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Forsberg, P., Hollman, P., and Jacobson, S., (2011). Wear mechanism study of exhaust valve system in modern heavy duty combustion engines. Wear, Volume:271, Number:9–10, pp:2477-2484. http://dx.doi.org/10.1016/j.wear.2010.11.039.