• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8888-4227
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0135
  • Page Number : 44-56
  • Doi : 10.12739/NWSA.2018.13.1.2A0135
  • Abstract Reading : 694
  • Download : 179
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 1
  • Number of Articles Published : 7
  • Published Date : 1.01.2018

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

PP VE PP/TALK KOMPOZİTLERİN MEKANİK VE KÖPÜKLENME ÖZELLİKLERİ ÜZERİNE ERGİYİK SICAKLIĞI VE ENJEKSİYON BASINCININ ETKİLERİNİN İNCELENMESİ

Salih Hakan YETGİN1 , Hüseyin Ünal2

Bu deneysel çalışmada, katkısız polipropilen (PP) termoplastik polimeri ve ağırlıkça %20 oranında talk katkılı polipropilen (PP-T) kompozit malzemesi kullanılmıştır. Köpük ajanı olarak endotermik tip kimyasal köpük ajanı kullanılmıştır. Enjeksiyon basıncı ve ergiyik sıcaklığı gibi üretim parametrelerinin katkısız polipropilen ve talk katkılı polipropilen kompozit köpük malzemelerin ortalama hücre boyutuna, hücre sayısına, köpük tabakası kalınlığına, köpük yoğunluğuna ve mekaniksel özelliklerine olan etkileri incelenmiştir. Elde edilen deney sonuçlarından ergiyik sıcaklığının artması ile hücre çapı artarken, malzeme yoğunluğu, kabuk tabakası kalınlığı, hücre yoğunluğu ve darbe dayanımı azalmıştır. Enjeksiyon basıncının artması ile köpük yoğunluğu, kabuk tabakası kalınlığı, hücre çapı ve darbe dayanımı azalırken, hücre yoğunluğu ise artmıştır.

Keywords
PP Köpük, Köpük Ajanı, Hücre Morfolojisi, Mekanik Özellikle, Kompozit,

INVESTIGATION OF THE EFFECT OF INJECTION PRESSURE AND MELT TEMPERATURE ON FOAMMABILITY AND MECHANICAL PROPERTIES OF PP AND PP/TALC COMPOSITE

Salih Hakan YETGİN1 , Hüseyin Ünal2

In this study, pure polypropylene (PP) thermoplastic polymer and 20% by weight of talc filled polypropylene (PP-T) composite material are used. Endothermic chemical foaming agents are used as a foaming agent. The injection pressure and melt temperature in the injection foam manufacturing process are just two of several important parameters. The effects of the injection pressure and melt temperatures of the production parameters, such as of average cell size, cell number, the foam layer thickness, foam density and mechanical properties were investigated on neat polypropylene and talc added polypropylene composite foam material. As a result, cell diameter increased with increasing melt temperatures while foam density, skin layer thickness, cell density and impact resistance decreased. By increasing injection pressure, foam density, skin layer thickness, cell diameter and impact resistance decreased while cell density increased.

Keywords
PP Foam, Foaming Agent, Cell Morphology, Mechanical Properties, Composite,

Details
   

Authors

Salih Hakan YETGİN (1) (Corresponding Author)
Dumlupınar University
shyetgin@gmail.com | 0000-0002-6068-9204

Hüseyin Ünal (2)

unal@sakarya.edu.tr | 0000-0003-0521-6647

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Pop-Iliev, R. and Park, C.B., (2002). Melt Compounding Based Rotational Foam Molding Technology for Manufacture of Polypropylene Foams. Journal of Reinforced Plastics and Composıtes, Volume:21, Number:2, pp:101-120.