• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : NWSA-268-287
  • Article Type : Araştırma Makalesi
  • Publication Number : A0104
  • Page Number : 627-635
  • Doi : 10.12739/
  • Abstract Reading : 1328
  • Download : 166
  • Share :

  • PDF Download

Issue Details

  • Year : 2008
  • Volume : 3
  • Issue : 4
  • Number of Articles Published : 6
  • Published Date : 1.10.2008

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ

Ali Kaya GÜR 1 , Tülay YILDIZ 2

Bu çalışmada; yüksek Cr’lu FeCrC tozu 0,3 C’lu çeliğin yüzeyine Plazma Transfer Ark (PTA) yöntemiyle kaplanmıştır. PTA yöntemiyle alaşımlandırılmış kaplama tabakaların aşınma yüzeylerinin SEM-EDS ve XRD analizleri incelenmiştir. Sonuç olarak; kaplama tabakasında metal karbürler ve nitrürlerin oluştuğu görülmüştür. Kaplama tabaksı farklı yük ve mesafelerde abrasiv aşınma testine tabi tutulmuştur. Kaplamanın karbür ve nitrür oranına bağlı olarak kaplama tabakasının sertliğinin ve aşınma direncinin arttığı görülmüştür.

Keywords
PTA,, FeCrC,, N2,, Cr(C,N), AŞINMA,

THE EFFECT AT WEAR BEHAVİOR OF COATİNG LAYER OF PROPORTİON GASES N2

Ali Kaya GÜR 1 , Tülay YILDIZ 1

In this study, high Cr at FeCrC powder was coated on the surface 0,3 C steel with PTA (plasma tungsten arc) method. The surfaces coated with PTA method were exanimate of surface wear SEM-EDS and XRD analysis.As a result of; in the coated layer was observer metal carburs and nitrurs. Coated layer were different loads and distancies of abrasive wear. Coating layer was observed increase of wear resistance and hardness to be proportions carburs and nitrurs.

Keywords
PTA, FeCrC, N2, Cr(C,N), Wear,

Details
   

Authors

Ali Kaya GÜR (1) (Corresponding Author)
Fırat Üni. Teknoloji Fak.Metalurji Malz Müh.
alikayagur@gmail.com

Tülay YILDIZ (2)

Fırat Üniversitesi
tyildiz@firat.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References