• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-7652-4254
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0100
  • Page Number : 98-109
  • Doi : 10.12739/NWSA.2016.11.4.2A0100
  • Abstract Reading : 533
  • Download : 124
  • Share :

  • PDF Download

Issue Details

  • Year : 2016
  • Volume : 11
  • Issue : 4
  • Number of Articles Published : 6
  • Published Date : 1.10.2016

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

LAZER KAYNAĞI İLE BİRLEŞTİRİLEN AISI 2205 DUBLEKS PASLANMAZ ÇELİĞİN MEKANİK VE MİKROYAPI ÖZELLİKLERİNİN İNCELENMESİ

Ceyhun KÖSE1 , Ramazan Kaçar 2

Bu çalışmada, AISI 2205 dubleks paslanmaz çelik levhalar CO2 lazer ışını kaynak yöntemiyle %50 Ar + %50 He gaz korumalı ortamda, 4000W lazer gücüyle ve 90cm/dk kaynak hızıyla birleştirilmiştir. Kaynaklı birleştirmelerin mekanik özelliklerini belirleyebilmek için çekme ve çentik darbe testleri uygulanmıştır. Kaynaklı bağlantının sertlik ölçümü kaynak yönüne dik kesitten gerçekleştirilmiştir. Mikroyapı karakteristikleri ise Optik mikroskop, Taramalı Elektron Mikroskobu (SEM), Enerji Dağılımlı X-Işını Spektroskopisi (EDS) ve XRD vasıtasıyla incelenmiştir. Sonuç olarak, CO2 lazer kaynak yöntemi ile birleştirilen dubleks paslanmaz çelik kaynak metali ve ısı tesiri altındaki bölgenin (ITAB) düşük ısı girdisine bağlı yüksek soğuma oranından etkilenerek final yapısının ferrit lehine değiştiği tespit edilmiştir. Kaynaklı birleştirmenin mekanik özellikleri kabul edilebilir değerlerde bulunmuştur.

Keywords
Paslanmaz Çelik , AISI 2205, CO2 Lazer Kaynağı, Mekanik Özellikler, Mikroyapı,

INVESTIGATION OF THE MECHANICAL AND MICROSTRUCTURAL PROPERTIES OF LASER BEAM WELDED AISI 2205 DUPLEX STAINLESS STEEL

Ceyhun KÖSE1 , Ramazan Kaçar 2

In this study, AISI 2205 duplex stainless steel plates were joined with CO2 Laser Beam Welding (LBW) method. The welding process were carried out in 50% Ar+50% He shielding gas atmosphere by using 4000W laser power for 90 cm/min welding speed. In order to determine the mechanical properties of laser welded joints, the tensile and charpy impact tests were applied. The hardness of the welded sample was measured on the cross section. The microstructure characterization of welded sample was carried out using with optical microscope, scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS) and XRD analysis. As a result of this study, the final microstructure of weld metal and heat affected zone (HAZ) were significantly affected on the favour of ferrite phase due to low heat input that caused high cooling rate in the solidification of CO2 laser welded duplex stainless steel. The mechanical properties of welded sample were found acceptable.

Keywords
Stainless Steel, AISI 2205, CO2 Laser Beam Welding, Mechanical Properties, Microstructure,

Details
   

Authors

Ceyhun KÖSE (1) (Corresponding Author)
Tokat Gaziosmanpaşa University
ceyhunia@gmail.com | 0000-0002-3907-2226

Ramazan Kaçar (2)

rkacar@karabuk.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Yang, S.M., Chen Y.C., Pani Y.T., and Lin, D.Y., (2016). Effect of Silver on Microstructure and Antibacterial Property of 2205 Duplex Stainless Steel, Materials Science and Engineering: C, Vol:63, 376-383.