• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8167-5453
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0136
  • Page Number : 57-66
  • Doi : 10.12739/NWSA.2018.13.1.2A0136
  • Abstract Reading : 449
  • Download : 106
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 1
  • Number of Articles Published : 7
  • Published Date : 1.01.2018

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

Sİ3N4 TAKVİYESİYLE ATIK ALÜMİNYUMDAN ÜRETİLMİŞ KOMPOZİTLERİN ÖZELLİKLERİNİN İNCELENMESİ

Burak ÖZTOP1 , Mevlüt Gürbüz 2

Bu çalışmada, pahalı saf alüminyum veya ticari alüminyum alaşımları yerine atık alüminyum içecek kutularından elde edilen matrise ağırlıkça %0-3 arasında silisyum nitrür (Si3N4) ilave edilerek karıştırmalı döküm yöntemi ile kompozit üretimi gerçekleştirilmiş ve takviye oranlarının üretilen kompozitlerin yoğunluk, sertlik ve mikroyapıya etkisi araştırılmıştır. Kompozitlerde ağırlıkça %1 Si3N4 takviyesine kadar sertliğin 70HV’den 87.9HV’ye arttığı belirlenmiştir. Mikroyapı analizlerinden, takviye elemanının homojen olarak dağıldığı, ancak ağırlıkça %1 oranından sonra tozların topaklandığı görülmüştür. Bu da hem mikroyapıyı hem de sertliği olumsuz etkilemiştir. Ayrıca yapılan yoğunluk ölçümleri sonucunda yoğunluğun genel olarak 2.53g/cm3, porozitenin ise %6.3 olduğu tespit edilmiştir.

Keywords
Atık Alüminyum İçecek Kutusu, Alüminyum Matrisli Kompozit, Karıştırmalı Döküm, Si3N4, Kompozit,

INVESTIGATION OF PROPERTIES OF COMPOSİTES PRODUCED FROM WASTE ALUMINUM WITH Si3N4 REINFORCEMENT

Burak ÖZTOP1 , Mevlüt Gürbüz 2

In this study, composites were produced by stir casting method by adding 0-3% of Si3N4 to matrix which obtained from waste aluminum beverage cans instead of expensive pure aluminum or commercial aluminum alloys. The effects of reinforcement ratio on density, hardness and microstructure of the produced composites were investigated. It has been determined that the hardness increases (from 70HV to 87.9HV) up to 1% Si3N4 reinforcement in composites. From the microstructure analysis, it was seen that the reinforcing element was homogeneously dispersed, but the powder was agglomerated after 1% by weight. This affects negatively both microstructure and hardness. In addition, density measurements showed that density and porosity were calculated as 2.53g/cm3 and %6.3.

Keywords
Waste Aluminium Beverage Can, Aluminum Matrix Composite, Stir Casting, Si3N4, Composite ,

Details
   

Authors

Burak ÖZTOP (1) (Corresponding Author)
Amasya University, burak.oztop@amasya.edu.tr, Amasya-Turkey
burak.oztop@amasya.edu.tr | 0000-0003-3947-9103

Mevlüt Gürbüz (2)

On Dokuz Mayıs University
mgurbuz@omu.edu.tr | 0000000323655918

Supporting Institution

 :

Project Number

 :

Thanks

 :
References