• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8822-4253
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0102
  • Page Number : 110-145
  • Doi : 10.12739/NWSA.2016.11.4.2A0102
  • Abstract Reading : 543
  • Download : 134
  • Share :

  • PDF Download

Issue Details

  • Year : 2016
  • Volume : 11
  • Issue : 4
  • Number of Articles Published : 6
  • Published Date : 1.10.2016

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

AlC İLAVE EDİLEN TOZ METAL ÇELİKLERDE KARBON ORANININ MİKROYAPI VE MEKANİK ÖZELLİKLER ÜZERİNE ETKİSİNİN ARAŞTIRILMASI

Mehmet Akif ERDEN1 , Mustafa TÜRKMEN2 , Hasan KARABULUT3 , Süleyman GÜNDÜZ4

Bu çalışmada, toz metalürjisi(TM)ile üretilen AlC ilave edilmiş çeliklerde karbon oranının mikroyapı and mekanik özellikler üzerine etkisi araştırılmıştır. Farklı karbon oranlarına sahip AlC ilave edilmiş TM çelik numuneler 750MPa presleme basıncında preslendikten sonra atmosfer kontrollü tüp fırında argon atmosferinde 1350°C sıcaklıkta 1 saat sinterlenerek üretimi gerçekleştirilmiştir. Üretilen farklı karbon oranlarına sahip AlC ilave edilmiş TM çeliklerinin tane boyutu ve fazların dağılımı optik mikroskop ile belirlenirken, mekanik özellikler çekme testi uygulanarak belirlenmiştir. Sonuçlar %0,55 karbon ilave edilmiş mikroalaşım çeliğinin en yüksek akma ve çekme dayanımı gösterdiği gözlenmiştir.

Keywords
Toz metalürjisi, Toz Metalürjisi Çelikleri, AlC, Mikroyapı, Mekanik özellikler,

INVESTIGATION OF THE EFFECT OF CARBON CONTENT ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AlC ADDED POWDER METALLURGY STEELS

Mehmet Akif ERDEN1 , Mustafa TÜRKMEN2 , Hasan KARABULUT3 , Süleyman GÜNDÜZ4

In this work, the effect of C content on the microstructures and mechanical behaviours of AlC added microalloyed powder metallurgy (PM)steels were investigated. The samples pressed at 750 MPa and sintered at 1350°C temperature in the sintering argon atmosphere for 1 h were produced. AlC added PM microalloyed steels with different carbon ratio were analysed in terms of grain size microstructure and tensile test. Results indicated that 0.55 wt. % C added PM steel showed the highest values in yield strength (YS) and ultimate tensile strength (UTS).

Keywords
Powder Metallurgy, , Powder Metallurgy Steels, ALC, Microstructure, Mechanical Properties,

Details
   

Authors

Mehmet Akif ERDEN (1) (Corresponding Author)
Karabük Üniversitesi
makiferden@karabuk.edu.tr | 0000-0003-1081-4713

Mustafa TÜRKMEN (2)

Kocaeli Üniversitesi
mustafa.turkmen@kocaeli.edu.tr | 0000-0002-9402-2459

Hasan KARABULUT (3)

Karabük Üniversitesi
karabulut.hasan@hotmail.com | 0000-0002-3370-9994

Süleyman GÜNDÜZ (4)

sgunduz@karabuk.edu.tr | 0000-0003-4285-5114

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Erden, M.A., (2015). Toz Metalürjisi Yöntemiyle Üretilen Mikroalaşım Çeliklerinin Mikroyapı Mekanik Özellik İlişkisinin Araştırılması, Doktora Tezi, Karabük Üniversitesi Fen Bilimleri Enstitüsü.