• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : NWSA-5287-2505
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0070
  • Page Number : 48-59
  • Doi : 10.12739/
  • Abstract Reading : 1100
  • Download : 126
  • Share :

  • PDF Download

Issue Details

  • Year : 2011
  • Volume : 6
  • Issue : 4
  • Number of Articles Published : 3
  • Published Date : 1.10.2011

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

AISI 304 OSTENİTİK PASLANMAZ ÇELİK YÜZEYİNİN FeTi+STELLİTE 6 ALAŞIMI KULLANILARAK YÜZEY MODİFİKASYONUNUN İNCELENMESİ

Mahmut KARATAŞ 1 , Hüseyin TURHAN 2

Bu çalışmada, AISI 304 ostenitik paslanmaz çelik yüzeyine FeTi +Stellite 6 alaşımı Tungsten Inert Gas (TIG) kaynak yöntemi kullanılarak alaşımlandırılmıştır. Kaplama tabakası; optik mikroskop (OM), taramalı elektron mikroskobu (SEM), X-ışın difraktogramı (XRD) ve X ışını enerji dağılım spektrometresinden (EDS) faydalanılarak incelenmiştir. Ayrıca numunelerin sertlik dağılımları mikro ve makro sertlik ölçümleri ile değerlendirildi. Optik mikroskop ve mikroyapı incelemeleri neticesinde, kaplama tabakası ile alt tabakanın birbirlerine metalurjik olarak bağlandığı, numunelerde, FeTi tozu ilavesine bağlı olarak sertlik değerlerinin arttığı ve tane sınırlarında ince taneli dentritik yapıların meydana geldiği tespit edilmiştir.

Keywords
AISI 304, Stellite 6, FeTi, TIG, Yüzey Modifikasyonu.,

THE INVESTIGATION SURFACE COATING USING FeTi+STELLITE 6 ALLOY OF AISI 304 AUSTENITIC STAINLESS STEEL SURFACE

Mahmut KARATAŞ 1 , Hüseyin TURHAN 1

In this study, FeTi with Stellite 6 alloy on the 304 austenitic stainless steel surface by using Tungsten Inert Gas (TIG) processing. Alloyed layer and interface were examined with optical microscope (OM), scanning electron microscope (SEM), and X-Ray diffraction (XRD) and energy dispersive spectograph. Macro and microhardness values of samples were measured. OM and SEM observations have been shown that the obtained coating had a smooth and uniform surface, as well as a metallurgical combination with the AISI 304 stainless steel substrate without cracks and pores at the interface. As a result of experimental study; hardness values of samples increased and the grain boundaries were occurred dendritic structures has been determined

Keywords
AISI 304, Stellite 6, FeTi, TIG, Surface Coating,

Details
   

Authors

Mahmut KARATAŞ (1) (Corresponding Author)
mahmutkaratas23@gmail.com

Hüseyin TURHAN (2)

Fırat Üniversitesi
hturhan@firat.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References