• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8010-4212
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0142
  • Page Number : 122-133
  • Doi : 10.12739/NWSA.2018.13.2.2A0142
  • Abstract Reading : 704
  • Download : 149
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 2
  • Number of Articles Published : 14
  • Published Date : 1.04.2018

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

SIC TAKVIYELİ ALÜMINYUM ESASLI KOMPOZITLERIN MEKANİK ÖZELLİKLERİNİN VE MİKRO YAPISININ İNCELENMESİ

Mahmut Can ŞENEL1 , Mevlüt Gürbüz 2 , Erdem KOÇ3

Bu çalışmada, toz metalürjisi metoduyla alüminyum matrise ağırlıkça %0-30 arasında değişen oranlarda SiC katkısı yapılmış olup takviye oranının deneysel yoğunluğa, Vickers sertliğine, basma dayanımına ve mikro yapıya olan etkisi incelenmiştir. Üretilen kompozitlerin karakterizasyon çalışmaları için X-ışını kırınımı (XRD) cihazı ve taramalı elektron mikroskobu (SEM) kullanılmıştır. SEM-EDX (enerji dağılımlı x-ışını) spektometresiyle yürütülen karakterizasyon çalışmalarında, SiC partiküllerin homojen şekilde dağıldığı görülmüştür. Mekanik testler neticesinde, üretilen saf alüminyumun Vickers sertliği 30 HV ve basma dayanımı 112 MPa iken; ağırlıkça %30 SiC katkısıyla Vickers sertliği 79 HV’ye ve basma dayanımı 221 MPa’a yükselmiştir. Sonuç olarak, SiC katkısının kompozitlerin mekanik özelliklerine olumlu yönde katkı yaptığı görülmüştür.

Keywords
Alüminyum, Silisyum Karbür, Toz Metalürjisi, Kompozit, Sertlik,

THE INVESTIGATION ON MECHANICAL PROPERTIES AND MICROSTUCTURE OF SIC REINFORCED ALUMINUM MATRIX COMPOSITES

Mahmut Can ŞENEL1 , Mevlüt Gürbüz 2 , Erdem KOÇ3

In this study, SiC was added to aluminum matrix by varying of 0-30%wt. Also, the effect of reinforcement ratio was investigated on density, hardness, compressive strength and microstructure. X-ray diffraction (XRD) device and scanning electron microscope (SEM) were used for the characterization of the composites. In the characterization studies carried out by SEM-EDX (energy dispersive x-ray) spectrometry, SiC particles were found to be homogeneously distributed. As a result of mechanical tests, the hardness and compressive strength value of pure aluminum was nearly 30 HV and 112 MPa. On the other hand, the hardness and compressive strength value of Al-30%SiC was nearly 79 HV and 221 MPa. In conclusion, it was seen that the addition of SiC positively contributes to the mechanical properties of the aluminum composites.

Keywords
Aluminum, Silicon Carbide, Powder Metallurgy, Composite, Hardness,

Details
   

Authors

Mahmut Can ŞENEL (1) (Corresponding Author)
Ondokuz Mayıs Üniversitesi
mahmutcan.senel@omu.edu.tr | 0000000000000000

Mevlüt Gürbüz (2)

On Dokuz Mayıs University
mgurbuz@omu.edu.tr | 0000000323655918

Erdem KOÇ (3)

erdemkoc@omu.edu.tr | 0000-0003-4892-7705

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Karabulut, H. and Çıtak, R., (2011). Alüminyum Matrisli ve SiC Parçacık Takviyeli Kompozitlerin Farklı Mekanik Alaşımlama Sürelerinde Üretilmesi ve Karakterize Edilmesi. 6th International Advanced Technologies Symposium. Elazığ. Bildiriler Kitabı, ss:527-530.