• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8572-4031
  • Article Type : Araştırma Makalesi
  • Publication Number : 1A0377
  • Page Number : 97-107
  • Doi : 10.12739/NWSA.2017.12.2.1A0377
  • Abstract Reading : 743
  • Download : 147
  • Share :

  • PDF Download

Issue Details

  • Year : 2017
  • Volume : 12
  • Issue : 2
  • Number of Articles Published : 4
  • Published Date : 1.04.2017

Cover Download Context Page Download
Dergi Kapağı
Engineering Sciences

Serial Number : 1A
ISSN No. : 1308-7231
Release Interval (in a Year) : 4 Issues

ASİDİK ORTAMDA YUMUŞAK ÇELİĞİN KOROZYONUNA İNHİBİTÖR OLARAK 2.5-DİKLOROANİLİN TÜREVLİ BİR SCHIFF BAZININ ADSORPSİYONUNUN ELEKTROKİMYASAL YÖNTEMLERLE İNCELENMESİ

Demet ÖZKIR1 , ÖMER ÇIFÇIBAŞI2

2.5-Dikloroanilin türevli yeni bir Shiff bazı (DCA) literatür metotlarına göre sentezlenmiş ve DCA’nın 1.0 M HCl çözeltisi içerisindeki yumuşak çeliğin korozyonuna inhibitör etkisi, elektrokimyasal impedans spektroskopisi (EIS), lineer polarizasyon direnci (LPR) ve potansiyodinamik polarizasyon eğrileri yöntemleriyle belirlenmiştir. Elektrokimyasal ölçümler, 298 K’de DCA’nın farklı derişimleri için gerçekleştirilmiştir. Farklı derişimlerin çeşitli zaman parametreleriyle değişimi EIS ile incelenmiş ve elde edilen Nyquist eğrilerinin, düzgün yarım daire şeklinde olmadığı yarı-elips şeklinde oldukları görülmüştür. Çalışılan tüm derişimlerde, zamana bağlı olarak inhibisyon etkinliği (%İE) değerlerinin artışının, DCA moleküllerinin elektrot yüzeyine adsorpsiyonundan kaynaklandığı belirlenmiştir. DCA’nın adsorpsiyon mekanizmasını belirlemek için EIS yöntemiyle metalin sıfır yük potansiyeli saptanmıştır. Yumuşak çelik elektrotların yüzey morfolojileri, taramalı elektron mikroskobu (SEM) ile ve ayrıca atomik seviyeye yakın çözünürlüğe sahip üç boyutlu görüntüler elde edilebilen; yüzey özellikleri, yüzey morfolojisi ve yüzey pürüzlülüğü hakkında önemli bilgiler veren atomik kuvvet mikroskobu (AFM) ile görüntülenerek aydınlatılmıştır. EIS bulguları ile yüzey analizleri sonuçları birbirini destekler niteliktedir.

Keywords
Schiff Bazı, Korozyon, EIS, SEM, AFM,

THE INVESTIGATION OF THE ADSORPTION OF A SCHIFF BASE DERIVATED FROM 2.5-DICHLOROANILINE AS AN INHIBITOR ON MILD STEEL CORROSION IN ACIDIC MEDIUM BY ELECTROCHEMICAL METHODS

Demet ÖZKIR1 , ÖMER ÇIFÇIBAŞI2

According to literature methods, a new Schiff base derived from 2.5-Dichloroaniline was synthesized (DCA) and its inhibitor effect was determined on mild steel corrosion in 1.0 M HCl by electrochemical impedance spectroscopy (EIS), linear polarization resistance (LPR) and potentiodynamic polarization techniques. Electrochemical measurements were performed for different concentrations of DCA at 298K. The change of different concentrations with various time parameters was examined by EIS and it was seen that the obtained Nyquist curves were in the form of semi-ellipses which were not regular semicircles. At all studied concentrations, it was seen that the increase in IE% values with time was due to adsorption of DCA molecules on metal surface. In order to understand the adsorption mechanism of DCA, the zero charge potential of metal is performed by using EIS. The surface morphologies of all electrodes are illuminated by scanning electron microscopy (SEM) and also atomic force microscope (AFM) which gives important information about surface properties, surface morphology and surface roughness, which can obtain 3D-images with resolution close to atomic level. EIS findings and surface analysis results support each other.

Keywords
Schiff Base, Corrosion, EIS, SEM, AFM,

Details
   

Authors

Demet ÖZKIR (1) (Corresponding Author)
Niğde Ömer Halisdemir University
dozkir@ohu.edu.tr | 0000-0002-8096-5755

ÖMER ÇIFÇIBAŞI (2)

kimyaci_511@hotmail.com | 0000-0000-0000-0039

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Abd El-Lateef, H.M., Abu-Dief, A.M., Abdel-Rahman, L.H., Sanudo, E.C., and Aliaga-Alcalde, N., (2015). Electrochemical and Theoretical Quantum Approaches on the Inhibition of C1018 Carbon Steel Corrosion in Acidic Medium Containing Chloride Using some NEWLY SYNTHESIZED PHENOLIC Schiff BASES COMPOUNDS, Journal of Electroanalytical Chemistry, Volume:743, pp:120–133.