• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : FIRAT-AKADEMI-8875-4209
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0145
  • Page Number : 157-164
  • Doi : 10.12739/NWSA.2018.13.2.2A0145
  • Abstract Reading : 693
  • Download : 143
  • Share :

  • PDF Download

Issue Details

  • Year : 2018
  • Volume : 13
  • Issue : 2
  • Number of Articles Published : 14
  • Published Date : 1.04.2018

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

TOZ METALURJİSİ YÖNTEMİYLE ÜRETİLEN ZA27/GRAFEN NANOKOMPOZİTLERİN KOROZYON DAVRANIŞI

Emre Deniz YALÇIN1

Çalışmada ZA27 matris alaşımının grafen nanolevha ile takviyelendirilen nanokompozitler toz metalurjisi yöntemiyle üretilmiştir. Grafen nanolevha takviyeleri ağırlıkça %0-%1-%2-%3 oranlarında katılarak kompozit toz karışımları hazırlanmıştır. Kompozit toz karışımları bilyeli öğütücü kullanılarak mekanik alaşımlamaya tabi tutulmuştur. Mekanik alaşımlama yapılan kompozit toz karışımlarından 435°C’de 500MPa basınç altında sıcak preslemeyle nanokompozitler üretilmiştir. Üretilen nanokompozitlerin içyapıları ve korozyon davranışı incelenmiştir. Korozyon deneyleri %3.5 NaCl çözeltisinde potansiyel-dinamik korozyon ünitesinde gerçekleştirildi. Artan grafen nanolevha miktarıyla nanokompozitin korozyon direnci artığı görülmüştür.

Keywords
ZA27 Alaşımı, Grafen Nanolevha, Toz Metalurjisi, Korozyon, Nanokompozit,

CORROSION BEHAVIOR OF ZA27/GRAFEN NANOCOMPOSITES PRODUCED BY POWDER METALLURGY

Emre Deniz YALÇIN1

In this study, nanocomposites reinforced with graphene nanosheet of ZA27matrix alloy were produced by powder metallurgy method. Composite powder mixtures were prepared by adding graphene nanosheet reinforcements 0%-1%-2-3% by weight. The composite powder mixtures were mechanically alloyed using a ball mill. Nanocomposites were produced by hot pressing under pressure of 500MPa at 435°C from mechanical alloyed composite powder mixtures. Microstructure and corrosion properties of these nanocomposites was investigated. Corrosion tests were carried out in a potential-dynamic corrosion unit in a 3.5% NaCl solution. The results indicated that increasing the amount of graphene nanosheet increased the corrosion resistance of the nanocomposite.

Keywords
ZA27 Alloy, Graphene Nanosheet, Powder Metallurgy, Corrosion, Nanocomposites,

Details
   

Authors

Emre Deniz YALÇIN (1) (Corresponding Author)
Karadeniz Teknik University
emredenizyalcin@ktu.edu.tr | 0000-0001-9691-1017

Supporting Institution

 :

Project Number

 :

Thanks

 :
References
[1] Türk, A., Kurnaz, C.., Sevik, H., (2007). Comparison of The Wear Properties of Modified ZA-8 Alloys and Conventional Bearing Bronz. Materials & Design 28(6) 1889–1897.