• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : NWSA-76-179
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0046
  • Page Number : 160-177
  • Doi : 10.12739/
  • Abstract Reading : 1526
  • Download : 186
  • Share :

  • PDF Download

Issue Details

  • Year : 2010
  • Volume : 5
  • Issue : 2
  • Number of Articles Published : 11
  • Published Date : 1.04.2010

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

CO2 LAZER IŞIN KAYNAĞI İLE BİRLEŞTİRİLEN FARKLI MALZEMELERİN (AISI 430-AISI 304) MİKROYAPI VE MEKANİK ÖZELLİKLERİNE YÜKSEK İLERLEME HIZININ ETKİSİ

Uğur ÇALIGÜLÜ 1 , Halil DİKBAŞ 2 , Mustafa TAŞKIN 3

Bu çalışmada, CO2 lazer ışın kaynağı ile kaynak edilen farklı malzemelerin(AISI 430-AISI 304) mikroyapı ve mekanik özelliklerine yüksek ilerleme hızının etkisi incelenmiştir. Lazer kaynakları, argon ve helyum koruyucu gaz atmosferlerinde, 2250 W sabit kaynak gücünde ve 100–200–300 cm/dk ilerleme hızlarında yapılmıştır. Kaynak sonrası birleşme ara yüzeyinde ve ısının tesiri altında kalan bölgede(ITAB) meydana gelen mikroyapı değişiklikleri optik mikroskop, SEM, EDS ve X-Ray analizleri ile incelenmiştir. Malzemenin birleşme mukavemetini belirlemek için çekme deneyi yapılmıştır. Yapılan incelemeler sonrasında bütün kaynaklarda, artan ilerleme hızına paralel olarak kaynak bölgesinin genişliğinin azaldığı tespit edilmiştir. Çekme testleri de bu sonucu doğrulamaktadır. Helyum atmosferi altında ve 100 cm/dk ilerleme hızı uygulanarak yapılan lazer kaynağının, metalurjik ve mekanik açıdan kaynak kalitesi en yüksek birleştirme olduğu tespit edilmiştir.

Keywords
Farklı Malzemeler (AISI 430–304), CO2 LBW, Kaynak Hızı, Mikroyapı, Mekanik Özellikler,

THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD

Uğur ÇALIGÜLÜ 1 , Halil DİKBAŞ 1 , Mustafa TAŞKIN 1

In this study, the effects of high welding speed on microstructure and mechanical property of dissimilar welded components (AISI 430 ferritic stainless steel and AISI 304 austenitic stainless steel) by CO2 laser welding was carried out. Laser beam welding experiments were carried out under argon and helium atmospheres at 2250 W constant heat input and 100-200-300 cm/min. welding speeds. The microstructures of the welded joints and the heat affected zones (HAZ) were examined by optical microscopy, SEM, EDS and X-Ray analysis. The tensile strength of the welded joints was measured. The result of this study indicated that; the width of welding zone became much thinner depending on the increased welding speed. Tensile strength values also confirmed this result. The best properties were observed at the specimens welded under helium atmosphere, at 100 cm/min welding speed.

Keywords
Dissimilar Components (AISI 430-304), CO2 LBW, Welding Speed, Microstructure, Mechanical Property,

Details
   

Authors

Uğur ÇALIGÜLÜ (1) (Corresponding Author)
Fırat University
ucaligulu@firat.edu.tr | 0000-0003-4862-7219

Halil DİKBAŞ (2)

Fırat University
hdikbas@firat.edu.tr | 0000-0001-9918-6631

Mustafa TAŞKIN (3)

Fırat Üniversitesi Teknoloji Fakültesi
mtaskin@firat.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References