• icon+90(533) 652 66 86
  • iconnwsa.akademi@hotmail.com
  • icon Fırat Akademi Samsun-Türkiye

Article Details

Article Details

  • Article Code : NWSA-808-523
  • Article Type : Araştırma Makalesi
  • Publication Number : 2A0009
  • Page Number : 98-108
  • Doi : 10.12739/
  • Abstract Reading : 1395
  • Download : 236
  • Share :

  • PDF Download

Issue Details

  • Year : 2009
  • Volume : 4
  • Issue : 2
  • Number of Articles Published : 16
  • Published Date : 1.04.2009

Cover Download Context Page Download
Dergi Kapağı
Technological Applied Sciences

Serial Number : 2A
ISSN No. : 1308-7223
Release Interval (in a Year) : 4 Issues

MERMER TOZU KATKILI KERPİÇİN MÜHENDİSLİK ÖZELLİKLERİNİN ARAŞTIRILMASI

Ömer Can 1 , Hasbi YAPRAK 2

Bu çalışmada, Afyon yöresindeki mermer fabrikalarından çıkan atık mermer tozunun kerpicin fiziksel ve mekanik özelliklerine etkisi araştırılmıştır. Mermer tozu, deneyde kullanılan kile ağırlıkça %5, %10, %15, %20, %25 oranlarında eklenerek, her bir karışımdan 70x70x70 mm ve 40x40x160 mm boyutunda 6’şar adet numune üretilmiştir. Numunelere; birim ağırlık, şişme, ultrases, büzülme, basınç dayanımı, çekme dayanımı, çamurlaşma ve kılcallık testleri uygulanmıştır. Yapılan deneyler sonucunda, %20 mermer tozu katkılı kerpicin en yüksek değerleri verdiği; birim ağırlığın 2,10 gr/cm3, şişme süresinin 6 dakika, ultrases geçiş hızının 1,21 km/s, basınç dayanımının 10,71 N/mm2, eğilmede çekme dayanımının 2,47 N/mm2, çamurlaşma süresinin 23 dakika, kılcallık değeri 20. dakikada 4cm olduğu görülmüştür.

Keywords
KERPİÇ, Mermer tozu, Kil oranı, KERPİÇ, MERMER TOZU,

INVESTIGATION OF ENGINEERING PROPERTIES OF ADOBE-MIXED GROUND MARBLE

Ömer Can 1 , Hasbi YAPRAK 1

In this study, the impact of ground marble released from the marble factories around the province of Afyon on mechanical and physical properties of adobe was investigated. For this purpose, ground marble was mixed with the clay used in the experiment at the rates of 5, 13, 15, 20 and 25 respectively; and from each of these mixtures 6 samples with different sizes (70x70x70mm and 40x40x160mm) were produced. Unit weight, swelling, ultrasound, shrinkage, compressive strength, tensile strength, mudding and capillarity tests were applied to these samples. As a result of the experiments carried out, it was observed that adobe mixed with 20% ground marble had the highest values with the unit weight of 2,10gr/cm3; swelling duration of 6 minutes; ultrasound velocity of 1,21km/s; compressive strength of 10,71N/mm2; tensile strength of 2,47 N/mm2; softening duration in water of 23 seconds; capillarity of 20 minutes .

Keywords
Adobe, Ground marble, Clay ratio, Adobe, Ground marble,

Details
   

Authors

Ömer Can (1) (Corresponding Author)
omercan@gazi.edu.tr

Hasbi YAPRAK (2)

Kastamonu Üniversitesi
hyaprak@kastamonu.edu.tr

Supporting Institution

 :

Project Number

 :

Thanks

 :
References